Wire rod

Wire rod


Hot-rolled structural alloy steel for cold extrusion and upsetting in coils Hot-rolled structural alloy steel for cold extrusion and upsetting in coils
ORDER
Range:
Ø 6,0; 6,5; 7,0; 7,5; 8,0; 8,5; 8,8; 9,0; 9,5; 10,0; 11,0; 11,5; 12,0; 12,5; 13,0; 13,5; 14,0; 16,0; 16,5; 18,0; 18,5 mm
Steel grade:
20G2P
Standard:
TU14-1-4486-88 rev. 2, 4, 7, 8, 9

Steel grade Cold-worked calibrated rolled metal Heat-treated calibrated rolled metal
Hardness number Tensile strength δB N/mm2 (kgf/mm2), no less Relative elongation, % Contraction,% Hardness number Tensile strength δB N/mm2 (kgf/mm2), no less Relative elongation, % Contraction,%
no less no less
20G2R 220 750(76) 18 45 163 540(55) 22 55

In coils with single banding by steel strap 0,8-1,0х32 mm or by wire rod 8.0 mm in 4 places min. equally distributed over coil. Outer diameter of a coil –1300 mm max., inner diameter – 820 mm min.

Option 1 – coil weight 1400-1800 kg.
Option 2 – coil weight 1800-2500 kg.

In the rolling mill line there is a system of technical control "HiTEST" for linear determination of surface defects on the rolling material without physical contact with the material. The "HiTEST" system is specially designed to detect surface defects of the rolling material: cracks, bubbles, voids, scale residues and exfoliation.

To monitor production processes and evaluate the quality of finished products, there are laboratories that conduct physical, mechanical, chemical and metallographic tests. The CPL laboratories are accredited for technical competence in the main activities in accordance with the requirements of the national standard STB / ISO IEC 17025 and the standard DIN EN ISO 17025:2005.

Product catalogue
PDF - 4 Mb
Rolled products catalogue
PDF - 3,6 Mb
Pipe products catalogue
PDF - 5,58 Mb
Steel cord and wire production catalogue
PDF - 2,90 Mb
BMC holding product catalog
PDF - 1,15 Mb